Issue 46

T. Bounini et alii, Frattura ed Integrità Strutturale, 46 (2018) 1-13; DOI: 10.3221/IGF-ESIS.46.01 2 front to the back of the tool where it consolidates. As cooling occurs, a solid continuous joint between the two plates is formed. No melting occurs during the process, and the resulting temperature remains below the solidus temperature of the metals being joined. FSW offers many advantages over conventional welding techniques, and has been successfully applied in the aerospace, automobile, and shipbuilding industries. Thermal and mechanical behaviors are mutually dependent during the FSW process. Because the temperature field affects stress distribution, this example uses a fully thermo-mechanically coupled model. The model consists of a coupled-field solid element with structural and thermal degrees of freedom. The model has two rectangular steel plates and a cylindrical tool. All necessary mechanical and thermal boundary conditions are applied on the model. The simulation occurs over three load steps, representing the plunge, dwell, and traverse phases of the process (Fig. 1) [1]. Figure 1: Schematic drawing of FSW process [2]. Numerical analysis of friction stir welding will allow many different welding processes to be simulated in order to understand the effects of changes in different system parameters before physical testing, which would be time-consuming or prohibitively expensive in practice [2]. This model assumes that two sheets of AA 5083 H111 are welded by a rotating tool. This model takes into account the actual interaction between the tool and the workpiece, and the deformation of the material around the tool. It should be noted that most of the finite element FE models, consider the two sheets as one, or simulate the heat flux without simulating the tool, or a part of the tool. The welding parameters, such as the variation of the welding speed, the rotation speed, and the material of the welded sheets, and their effects on the longitudinal stress, and on the distribution of the temperature flow. An experimental study was carried out, for the purpose of defining the impact of the change of welding parameters on the tenacity of welded joints. The friction stir welding is done using a milling machine. Fatigue and tensile tests were carried out on test tubes of material Alluminium alloy 6082-T6. E XPERIMENTAL STUDY ON AA6082-T6 ur study focuses on the characterization of two materials 6082-T6 (Base material and FSW welded material). The characterization tests are based on two essential tests, tensile test to identify the behavioral laws of the different materials and fatigue test to see the evolution of a crack in the different configurations. The chemical composition of the studied alloy is reported in the table below: Table 1 : The chemical composition of AA 6082-T6. Tensile Test For the different parts of the mechanical tests allowing the characterization of the materials, we carried out simple tensile tests on "dumbbell" specimens machined in aluminum sheets (longitudinal). The geometry of the specimens is described in Fig. 2. O Al Alloy Si Mg Fe Cu Mn Cr Zn Ti Al 6082-T6 1.3 1.2 0.5 0.1 1.0 0.25 0.2 0.1 98.3