Issue 52

M.F. Bouali et alii, Frattura ed Integrità Strutturale, 52 (2020) 82-97; DOI: 10.3221/IGF-ESIS.52.07 86 This Study try to figure out that these composite material models, mentioned above, got reliable prediction abilities for the modulus of elasticity of LWAC. The modulus of elasticity values were predicted utilizing the composite models and then, the predicted results were compared to the experimental results of De Larrard  7  , Yang and Huang  8  and Ke Y et al.  9  respectively. Ref. grav. d/D (mm) V g E g (GPa) E m (GPa) E exp_De Larrard (GPa) 8 Argi 16 8 Isol S 8 Leca 7j. 8 Leca 28j. 8 Surex 675 8 Galex 7j. 8 Galex 28j. 9 Schiste 15j. 9 Schiste 28j. 9 Leca 1j. 9 Leca 2j. 9 Leca 7j. 9 Leca 28j. 9 Leca 90j. 9 Surex 1j. 9 Surex 2j. 9 Surex 7j. 9 Surex 28j. 9 Surex 90j. 3 LWC1 Crush 3 LWC1 Crush 3 LWC1 Pellet 3 LWC1 Pellet 3 HSLWC Pel. 3 HSLWC Pel. 1 Liapor 2 Liapor 16 Javron 16 G/S -0.2 16 G/S +0.2 16 EAU + 16 EAU – 4-12 3.15-8 4-10 4-10 6.3-10 3-8 3-8 - - 4-10 4-10 4-10 4-10 4-10 6.3-10 6.3-10 6.3-10 6.3-10 6.3-10 10-20 10-20 5-20 5-20 5-20 5-20 0-16 4-16 4-10 4-10 4-10 4-10 4-10 0.414 0.414 0.414 0.414 0.414 0.425 0.425 0.391 0.391 0.414 0.414 0.414 0.414 0.414 0.414 0.414 0.414 0.414 0.414 0.403 0.403 0.414 0.414 0.255 0.255 0.473 0.432 0.463 0.443 0.478 0.473 0.453 8 13.1 7.6 7.6 16.2 33 33 21 21 8.6 8.6 8.6 8.6 8.6 19 19 19 19 19 13.6 13.6 14 14 14 14 21.5 21.5 16 16 16 16 16 25.2 25.2 23.5 25.2 25.2 20.6 21.9 24.9 25.6 11 15 20 25.2 31 11 15 20 25.2 31 33.2 33.2 32.8 32.8 38.5 38.5 29.7 27.9 23.8 24.6 23.1 26.6 21.1 15.6 19.2 14.1 15.7 21 25.5 25.8 23.9 23.4 10 12 13.9 16 17.8 14.6 17.1 20.6 22.3 22.6 23 24.3 22.7 24.3 27.6 28.3 25.5 24.8 19.7 19.9 19.7 20.9 18.1 Table 1: Characteristics of LWAC tested by De Larrard  7  . Ref. grav. d/D (mm) V g E g (GPa) E m (GPa) E exp_Yang (GPa) A3 A4 A5 A6 5-10 0.18 0.24 0.30 0.36 6.01 6.01 6.01 6.01 29.33 28.13 26.44 24.87 23.020 20.600 18.210 15.800 B3 B4 B5 B6 0.18 0.24 0.30 0.36 7.97 7.97 7.97 7.97 29.33 28.13 26.44 24.87 23.790 21.530 19.010 17.220 C3 C4 C5 C6 0.18 0.24 0.30 0.36 10.48 10.48 10.48 10.48 29.33 28.13 26.44 24.87 24.660 22.580 20.320 18.650 Table 2: Characteristics of LWAC tested by Chung-Chia Yang and Ran Huang  8  .