Issue 48

X.-g. Huang et alii, Frattura ed Integrità Strutturale, 48 (2019) 48 1 -490; DOI: 10.3221/IGF-ESIS.48.46 483 loading frequencies are set as 0.5, 1 and 2Hz, respectively. To ensure the interaction of sample and corrosion solution during the fatigue test. A special designed circulating device of seawater is used to maintain the circulation and renewal of the seawater, as shown in Fig. 2. The pump drives corrosive liquid circulate in the tube, and spray it on the test section of the samples through the shower. The surface of testing section of the sample is strapped with a layer of absorbent fiber to ensure the full immersion of the samples in the absorbed solution during the experiment. Figure 2: Setup of circulation device of corrosion solution. Results of corrosion fatigue tests Fig. 3 shows the number of cycles to fatigue and corrosion fatigue failure for bare AH 32 steel in seawater under different stress amplitudes. It can be seen corrosion environment impose an obvious influence on fatigue life, and this effect becomes more significant at low stress level. Stress amplitude is the dominant factor determining fatigue and corrosion fatigue life, and fatigue lives increase with the decrease of stress amplitude. The stress frequency also has a significant effect on the corrosion fatigue life, and the corrosion fatigue lives decrease at lower frequencies under the same stress amplitude. It can be explained that the interaction between sample and corrosion environment is more effective in each cycle at low frequencies, which accelerates the evolution of corrosion fatigue damage per cycle [26-27]. In contrast, the effect of frequency on fatigue life is not as significant as corrosion fatigue. Figure 3: Results of fatigue and corrosion fatigue tests. Fig. 4 shows the typical fracture surface of the sample under low stress amplitude. From the overall morphology of the fracture shown in Fig. 4(a), there shows symmetry of the morphological development on both sides, and the crack initiation zone, extension zone and fracture zone are in turn from the two sides to the central axis. Fig. 4 (b) shows the morphology of crack nucleation zone, and it can be seen clearly that the corrosion pit promotes the formation fatigue flow direction chuck recycling pump corrosive solution storage box tube seal ring shower fatigue sample absorbent fiber chamber 160 200 240 280 320 10000 100000 1000000 10000000 S /MPa N /cycle f=0.5Hz(fatigue) f=1Hz(fatigue) f=2Hz(fatigue) f=0.5Hz(corrosion fatigue) f=1Hz(corrosion fatigue) f=2Hz(corrosion fatigue)