Issue 42

D. V. Orlova et alii, Frattura ed Integrità Strutturale, 42 (2017) 293-302; DOI: 10.3221/IGF-ESIS.42.31 298 (a) (b) (c) (d) Figure 4 : Movement of localized plasticity domains at the stage n <0.5: a - for steel (G10080); b - for steel (AISI 420); c - for silicon iron; d - for steel (321H). For the obtained dependences   X t , the pole is not always identified. However, the position of poles can always be shown if the linear dependence (2) is met. Let us consider the calculation for steel (G10080). It is seen that the pole is reached at the moment of time 5978 s, and the self-consistent movement of the zones begins at t 0 = 4003 s (Fig. 4a). The coordinate of the stationary localization zone for steel (G10080) is Х S.Z . = 35.85 mm from the stationary testing machine head. According to the data in Tab. 3, the velocity of deformation zones was obtained versus the initial coordinates V aw (ξ) (Fig. 6). The constants α and 0  are determined experimentally by the method of least squares, in this case  0 = 0.0018 and  = 4.98·10 -4 . Fig. 6 also shows that the dependence   V  obtained for all test alloys is linear. Domain, № 1 2 3 4 5 ξ i , mm 26.47 20.58 15.19 6.48 0 V i × 10 6 , m·s -1 0.15 0.11 0.1 0.07 0.0031 Table 3 : Velocities of the deformation zones at the pre-fracture stage for steel (G10080). 3500 4000 4500 5000 5500 6000 5 10 15 20 25 30 35 40 5 4 3 2 1 t exp Coordinate (mm) Time (s) * 500 550 600 650 700 750 5 10 15 20 25 30 35 40 Coordinate (mm) Time (s) 1200 1400 1600 1800 2000 2200 2400 15 20 25 30 35 40 45 Coordinate (mm) Time (s) 5300 5400 5500 5600 5700 5 10 15 20 25 30 35 40 45 Coordinate (mm) Time (s)