U. Haider et alii, Frattura ed Integrità Strutturale, 38 (2016) 305-318; DOI: 10.3221/IGF-ESIS.38.41 312 Morphological properties, chemical composition and mineralogical properties Field emission electron microscope was used to determine the morphology of individual submicron and ultrafine particles present in the raw fly ash, second layer, and third layer particles (Fig.5). From FE-SEM images in Fig. 5(a) and (b) it can be observed that raw fly ash consists of micron, submicron and ultrafine size particles. FE-SEM images in Fig. 5(c) show that second layer particles consists of majority of submicron and ultrafine (<1µm) particles. In Fig. 5(d) submicron to ultrafine (<1µm) size particles can also be observed. Fig. 5(e) shows FE-SEM images of third layer particles consisting in much bigger in size as compared to those of second layer particles. In Fig. 5(f) it can be seen that particles of third layer contain significant amount of bright particles [44], which are absent in the images of second layer. FE-SEM images of Fig. 5(a), (c), and (e) were carried out in which maximum area at lowest possible magnification was covered in electron microscope in order to determine chemical composition of specimens, listed in Tab. 2. Tab. 3 shows that Amorphous, quartz (SiO 2 ), mullite (Al 0.69 Si 1.22 O 4.85 ), and magnetite (Fe 3 O 4 ) phases are present in raw fly ash, second layer, and third layer. Al Si K Ca Ti Fe Na Mg P Zr Raw fly ash 26.18 60.81 2.09 1.34 0.89 1.35 1.54 1.39 0.00 3.63 Second layer 25.97 60.29 3.19 1.88 0.96 0.93 0.74 0.72 0.83 2.71 Third layer 25.25 53.77 4.06 2.36 1.58 8.89 0.63 1.11 0.33 0.53 Ba Bi S V Cr Mn Co Ni Cu Zn Raw fly ash 0.00 0.29 0.00 0.00 0.00 0.03 0.00 0.06 0.07 0.13 Second layer 0.07 0.00 0.21 0.22 0.10 0.00 0.14 0.00 0.00 0.05 Third layer 0.00 0.00 0.22 0.08 0.00 0.17 0.00 0.01 0.03 0.14 Ga Ge As Se Rb Sr Y La Ce Hg Raw fly ash 0.11 0.03 0.00 0.05 0.30 0.00 0.00 0.00 0.00 0.00 Second layer 0.03 0.02 0.00 0.25 0.18 0.01 0.12 0.00 0.00 0.00 Third layer 0.02 0.00 0.00 0.00 0.00 0.00 0.00 0.09 0.00 0.25 Table 2 : Chemical composition from Energy Dispersive X-ray Spectrometry (EDX) analyses for raw fly ash, second layer particles, and third layer particles. Table 3 : X-ray Diffraction (XRD) mineralogical composition of raw fly ash, second layer particles, and third layer particles. Using EDX analyses, individual particles in raw fly ash of Fig. 5(b) were analysed with small area and point analyses for the composition of Si, Al, Fe, Ca and other twenty seven elements present in them. Ternary Si-Al-Fe diagram for raw fly ash, second layer, and third layer particles are shown in Fig. 6(a) - (b). Similarly ternary diagrams were plotted to compare the ratio of percentages of Si, Al, and Ca for raw fly ash, second layer, and third layer particles as shown in Fig. 6(c) - (d). Fig. 6(e) and (f) shows ternary diagram between Alkali and Alkaline metals (AAM), metalloids and non-metals (MNM), and transition heavy metals (THM) in particles of raw fly ash, second layer, and third layer particles. Specimen Amorphous (%) Quartz (%) Mullite (%) Magnetite (%) Raw fly ash 40 19 39 2 Second layer 45 17 37 1 Third layer 37 18 38 7