F.A. Stuparu et alii, Frattura ed Integrità Strutturale, 36 (2016) 69-77; DOI: 10.3221/IGF-ESIS.36.08 71 The single-lap joint prepared for DIC measurements is shown in Fig. 2. On the left side it is better noticed the uneven surface due to the wax of constant 0.5 mm thickness which filled the overlap for 5 mm on each side as to control the adhesive thickness. Figure 1 : Dimensions of the single-lap joints. Aluminium Carbon 3 mm Carbon 5 mm Modulus of elasticity [MPa] 70000 76000 64000 Poisson's ratio 0.33 0.35 0.37 Table 1 : Elastic constants of adherends. Figure 2 : Surface of a single-lap joint prepared for DIC measurements. Overall, six different geometrical configurations were used for testing, as mentioned in Tab.2. For each configuration five lap joints were tested. If the failure was not cohesive the test was disregarded. Adherend 1 Adherend 2 Material Thickness Material Thickness Configuration 1 aluminium 3 mm aluminium 3 mm Configuration 2 carbon 3 mm carbon 3 mm Configuration 3 aluminium 3 mm carbon 3 mm Configuration 4 aluminium 5 mm aluminium 5 mm Configuration 5 carbon 5 mm carbon 5 mm Configuration 6 aluminium 5 mm carbon 5 mm Table 2 : Configurations used for testing with aluminium and carbon adherends of different thickness.