Issue 36

R. Tovo et alii, Frattura ed Integrità Strutturale, 36 (2016) 119-129; DOI: 10.3221/IGF-ESIS.36.12 124 Tab. 2 shows the fatigue data obtained with a stress ratio R = -1. Specimen Range [MPa] Cycles Run out W115 102.94 697,953 W111 154.36 19,763 W127 138.92 81,298 W114 92.61 463,257 W123 77.18 2,000,000 x W116 92.61 2,000,000 x W119 154.36 17,200 W121 92.61 476,829 W125 82.35 2,000,000 x W115 102.94 697,953 Table 2: Fatigue data obtained at R = -1. C RACK INITIATION SITE rack initiation sites are defined in terms of their angular position relative to the end point of the weld, given as 0° in Fig. 7 where the advancing side of the weld is towards the top in the figure, and the retreating side is towards the bottom. Figure 7: Coordinate system used to define the crack initiation sites. Crack initiation was located in the advancing side of the weld in almost half of the specimens, usually closely associated with the slight undercut at the edge of the weld zone. Tab. 3 gives the location of crack initiation for all of the specimens where cracking was observed. In the two specimens that were left intact (W117: 709,775 cycles and W121: 476,829 cycles) cracking had initiated along the middle plane of the weld zone and one specimen fractured through the middle of the weld (W118: 1,247,627 cycles). The data is summarised in the bar chart shown in Fig. 8. C 0°