S. Kikuchi et alii, Frattura ed Integrità Strutturale, 34 (2015) 261 - 270; DOI: 10.3221/IGF-ESIS.34.28 261 Focussed on Crack Paths Evaluation of near-threshold fatigue crack propagation in Ti-6Al-4V Alloy with harmonic structure created by Mechanical Milling and Spark Plasma Sintering S. Kikuchi, T. Imai, H. Kubozono, Y. Nakai Department of Mechanical Engineering, Kobe University, 1-1 Rokkodai, Nada, Kobe, 6578501, Japan kikuchi@mech.kobe-u.ac.jp , 147t313t@stu.kobe-u.ac.jp, 159t323t@stu.kobe-u.ac.jp, nakai@mech.kobe-u.ac.jp A. Ueno, K. Ameyama Department of Mechanical Engineering, Ritsumeikan University ueno01@fc.ritsumei.ac.jp , ameyama@st.ritsumei.ac.jp A BSTRACT . Titanium alloy (Ti-6Al-4V) having a bimodal “harmonic structure”, which consists of coarse- grained structure surrounded by a network structure of fine grains, was fabricated by mechanical milling (MM) and spark plasma sintering (SPS) to achieve high strength and good plasticity. The aim of this study is to investigate the near-threshold fatigue crack propagation in Ti-6Al-4V alloy with harmonic structure. Ti-6Al-4V alloy powders were mechanically milled in a planetary ball mill to create fine grains at powder’s surface and the MM-processed powders were consolidated by SPS. K -decreasing fatigue crack propagation tests were conducted using the DC(T) specimen (ASTM standard) with harmonic structure under the stress ratios, R , from 0.1 to 0.8 in ambient laboratory atmosphere. After testing, fracture surfaces were observed using scanning electron microscope (SEM), and crack profiles were analyzed using electron backscatter diffraction (EBSD) to discuss the mechanism of fatigue crack propagation. Threshold stress intensity range,  K th , of the material with harmonic structure decreased with stress ratio, R , whereas the effective stress intensity range,  K eff , showed constant value for R lower than 0.5. This result indicates that the influence of the stress ratio, R , on  K th of Ti- 6Al-4V with harmonic structure can be concluded to be that on crack closure. Compared to the compact prepared from as-received powders with coarse acicular microstructure,  K th value of the material with harmonic structure was low. This was because the closure stress intensity, K cl , in the material with harmonic structure was lower than that of the coarse-grained material due to the existence of fine grains. In addition, the effects of the grain size on the fatigue crack propagation behaviors of Ti-6Al-4V alloy were investigated for the bulk homogeneous material. The effects of the stress ratio and the grain size on the fatigue crack propagation of the material with harmonic structure were quantified. K EYWORDS . Fatigue; Titanium alloy; Crack closure; Ultra-fine grain; Powder metallurgy; Harmonic structure.

RkJQdWJsaXNoZXIy MjM0NDE=