Issue 30

F. Felli et alii, Frattura ed Integrità Strutturale, 30 (2014) 48-54; DOI: 10.3221/IGF-ESIS.30.07 49 The Bartolomeo Colleoni monument suffered from years of neglect and damage from the local climate. In 2003 the World Monument Fund began the cleaning and restoring of the equestrian statue that was subjected to the last major conservation work in 1919 [1]. The process of restoring the Colleoni Monument allowed to understand how the bronze statue was originally cast and manufactured and the techniques used in its construction. These studies give a historical insight into the practice of skilled foundrymen and the technologies used for manufacturing big statues. Considering the impressive size of the statue, Verrocchio decided to use the lost-wax casting method for manufacturing different parts of the monument that would be subsequently joined by means of the cast-on method [2] used by the fifteenth century foundrymen to join two different castings. Therefore the equestrian monument of Bartolomeo Colleoni, that weighs about 6000 Kg, is composed of 14 different castings (8 for the horse and 6 for the rider). As far as the horse is concerned the single cast parts were: 1) right foreleg, 2) left foreleg; 3) right hind leg, 4) left hind leg, 5) front portion of the body; 6) rear portion of the body, 7) head, 8)tail. The cast-on method has to join the different parts in such a way that they fit closely and that joints are strong enough to support the monument weight. In fact the huge weight of the statue stands on a pedestal where three horse’s hoofs are placed at the vertexes of a slender triangle. During the restoration work of the Colleoni equestrian statue a system of FBG sensors has been applied for long-term structural health monitoring of a crack in the right foreleg [3-5]. The system allowed to verify the structural stress during sensor calibration performed by applying a mechanical stress on the riderless horse and during the rider repositioning [6,7]. FBGs are basically optical strain gages but offer several advantages over the conventional ones. The most interesting characteristics for the applications under concern are the possibility to multiplex dozens of them within the same fiber and the long term stability. One of the processes commonly used for the production of FBG is that one of using coherent UV light illuminating transversally the fiber. The interference pattern can be produced with a phase mask positioned just above the optical fiber. The result of the irradiation is the production of a periodic fluctuation of the index of refraction (called Bragg Grating) in the longitudinal direction of the fiber core. The property of the FBG is to reflect a specific wavelength called Bragg wavelength λ B if some broad-band light propagates along the optical fiber. Since the value of λ B is affected by strain according to a predictable relationships, measuring λ B allows measuring the strain of a structure to which the FBG has been attached with adequate structural contact [8,9]. C RACK MONITORING BY MEANS OF FBG SENSORS n the right foreleg in correspondence of the welding seam an extended crack affects almost the whole section of the thigh (Fig. 1). In some places the crack branches into two or more paths. This crack was probably formed already during the welding seam cooling, in fact it is possible to find in it shrinkage cavities. The reinforcement of the right foreleg with an internal iron bar (Fig. 2) suggests that Leopardi had already identified this crack. Figure 1 : Macrograph showing the crack in the right foreleg of the horse. Figure 2 : Detail of the internal part of the horse right foreleg showing the iron bar used as a reinforcement. O