Issue 36

F. Z. Liu et alii, Frattura ed Integrità Strutturale, 36 (2016) 139-150; DOI: 10.3221/IGF-ESIS.36.14 139 Effects of hydrogen induced delay fracture on high-strength steel plate of automobile and the improvement Fengzhu Liu, Yu Zhao Changchun Automobile Industry Institute, Changchun, Jilin, 130013, China zyzhaoyz@163.com A BSTRACT . Delay fracture is an environmental embrittlement occurring when materials, environment and stress interact with each other and also a form of hydrogen induced material deterioration. It is a leading factor inhibiting the further improvement of strength of steel and iron material. Hence this study analyzed the improved low-carbon Mn-B type ultra-high strength steel plate (1500 MPa) which were processed by conventional heat treatment and heating forming technique and explored the effects of tempering temperature and heating forming technique on the performance of hydrogen induced delay fracture, which provides a reference for the actual application of such kind of steel plate. K EY WORDS : Hydrogen induced delay fracture; Environmental management technology. I NTRODUCTION igh-strength steel is usually mixed with hydrogen during smelting, processing and using. Generally, hydrogen which enters steel is extremely harmful. For many materials, even a trace of hydrogen can induce delay fracture through diffusion and enrichment. Hence the diffusion and enrichment of hydrogen in metals is the premise and bridge for delay fracture [1-3]. Delay fracture of high-strength steel is a manifestation of hydrogen embrittlement of metals. According to the source of hydrogen, hydrogen embrittlement can be typed into environmental hydrogen embrittlement and internal hydrogen embrittlement [4 - 6]. Environmental hydrogen embrittlement is induced by the invasion of hydrogen generated from corrosion reaction which happens when materials are exposed to the air for a long time. For instance, delay fracture may happen to bolt used in bridge if it is exposed to moist air or rain. Internal hydrogen embrittlement is induced by the gathering of hydrogen that enters steels in the process of thermal processing, acid pickling and electroplating towards stress source [7 - 9]. For instance, electroplated bolt may crack in a short time after loading. Delay fracture can result in the damage of high-strength steels within the designed load-carrying capacity. Materials with higher grades are of higher risks of delay fracture. Delay fracture is difficult to be detected and usually happens suddenly [10]. Recently, accidents induced by hydrogen induced delay fracture of high-strength steels happen frequently. Delay fracture has become a barrier for the development of high-strength steel. A large number of evidences have suggested that, the delay fracture of high strength steel have brought huge threatens to industries such as modern motor, architecture, mechanics and light industry. When the strength of steel is over 1200 MPa, the steel would be highly sensitive to hydrogen induced delay fracture [11 - 12]. Till now, several researches have studied the delay fracture behavior of high-strength and ultra high strength steel plat [13]. However, we attach less importance to the delay fracture resistance of low-carbon Mn-B steel plate [14], especially the delay fracture performance of low-carbon Mn-B steel plate which has H